Custom 465 stainless is a premium melted, martensitic, age-hardenable alloy capable of ultimate tensile strength in excess of 250 ksi in the overaged (H 950) condition. This alloy was designed to have excellent notch tensile strength and fracture toughness in this condition. Overaging to the H1000 condition provides a superior combination of strength, toughness and stress corrosion cracking resistance compared with other high-strength PH stainless alloys such as Custom 455 stainless or 13-8 stainless.
The general corrosion resistance of Custom 465 stainless approaches that of Type 304 stainless. Exposure to 5% neutral salt spray at 95°F (35°C) (per ASTM B117) caused little or no rusting after 200 hours regardless of condition (i.e., annealed or H900-H1100 conditions).
| ALLOY | SIZE | WEIGHT |
|---|---|---|
| CURRENT BAR INVENTORY | ||
| Custom 465 | 0.260 DIA X 143" RL 6.604MM DIA | 1389 LBS 630 KG |
| Custom 465 | 0.510 DIA X 129-144RL 12.954MM DIA | 1484 LBS 673 KG |
| Custom 465 | 0.635 DIA X 127-145RL 16.129MM DIA | 1524 LBS 691 KG |
| Custom 465 | 0.760 DIA X 134-155RL 19.304MM DIA | 1267 LBS 575 KG |
| Custom 465 | 1.010 DIA X 126-155RL 25.654MM DIA | 1259 LBS 571 KG |
| Custom 465 | 1.260 DIA X 141-154RL 32.004MM DIA | 1664 LBS 755 KG |
| Custom 465 | 1.510 DIA X 131-155RL 38.354MM DIA | 1537 LBS 697 KG |
| Custom 465 - DUE DATE: 06-15-24 | 1.760 DIA X 160" RL 44.704MM DIA | 1667 LBS 756 KG |
| Custom 465 | 2.010 DIA X 154-155RL 51.054MM DIA | 1796 LBS 815 KG |
| Custom 465 | 2.510 DIA X 114-145RL 63.754MM DIA | 1548 LBS 702 KG |
| Custom 465 - DUE DATE: 06-15-24 | 2.510 DIA X 132" RL 63.754MM DIA | 4800 LBS 2177 KG |
| Custom 465 | 3.020 DIA X 143-148RL+112 76.708MM DIA | 1697 LBS 770 KG |
| Custom 465 - DUE DATE: 06-15-25 | 3.520 DIA X 132" RL 89.408MM DIA | 4500 LBS 2041 KG |
| Custom 465 - DUE DATE: 05-15-24 | 4.020 DIA X 132" RL 102.108MM DIA | 4500 LBS 2041 KG |